重力分離shs法制備陶瓷復合鋼板的理論和實驗研究

1、363863論文題目：重力分離SHS法制備陶瓷復合鋼板的理論和實驗研究TheTheoreticandExperimentalResearchofCeramic——CompositedSteelPlateProducedbySHSGravitationalSeparationProcess研究生姓名：楊似瓊指導教師姓名：王凰監(jiān)直送蝗單位：轅出型堇盤堂——論文提交日期學位授予日期論文評閱人答辯日期授予單位單位單位鞍山科技大學碩士學位論文Ab

2、stractThecarbon—steelplatehassuperficialmodificationbypreparingceramiccoating，whichcanbetheconstructionalmaterialofthemechanicalequipments，andCanbewidelyusedforwearableorcorrosionresistantpartsinallkindsofplants，SOthatab

3、rasionresistanceofcomponentsandpartsislargelyenhanced，andSOisthelongevityofcompletemachinesComparedwiththetraditionaltechnologyofwearablematerialpreparation，themeritsofSHS—Gravitationalprocessaresimplytechnologicalproces

4、s，lowenergyconsumption，higherproductionefficiencyandSOonTherefore，thetechnologicalparameterofproducingceramic—compositedsteelplatebySHSGravitationalseparationtechnologyisworthywhiletesearchInthisthesis，twomethodsofprepar

5、ingceramic—compositedsteelplatebySHS—GravitationalseparationprocessweresystemataciallystudiedOntheconditionofputtingthecoreinthemiddleofbig—sectionsquarepipe，theceramiclinedsteelpipesweremade，whichcouldbedirectlyused，als

6、obecutintotheceramic—compositedsteelplatewithcrimpingTheotheroneisthatindomesticandforeignresearch，theceramic—compositedcoatingwasdirectlycoatedonthesteelplatewithcrimpingforthefirsttime，whichhadwellbondandgoodqualityWef

7、oundthatinfluencingfactorsoncoatingthicknessandhardnesswerechemicaladditive，filingdensitypreheating，ratiopowderweighttovolumeofbasal—bodygranularity，corematerial，mixturetimeandSOon，andgoodmethodsofpreparingtheceramiccomp

8、oundsteelplatewereownedThecompositionandmicrostructurewereanalyzedbyusingXRD，electronmicroscope，andcombinationintensitiesbetweenceramiccoatingandbasalbodyweremeasuredonthenormalandtangentdirection，thecombinationwayswered

9、eterminedTheformingprocessandqualityinfluenceofirongrainintheceramicwereanalyzedWecomparedcommercialFe203powderwithchemistryFe203powderonthicknessuniformity，hardnessandcombinationintensityoftheceramic—coatingproducedbyth

10、emjandtheresearchfoundationofindustrializedproductionwasestablishedThecoolingprocessoftheceramic—linedsquarepipeswassimulatedbyANSYSanalysissoftwareTemperaturetimecurvesofcompositedsquarepipeswithdifferentthicknessandres